Interaction of stress corrosion cracks in single crystals Ni-Base superalloys
dc.contributor.author | Elsherkisi, Mustafa | |
dc.contributor.author | Martinez, Fabian Duarte | |
dc.contributor.author | Mason-Flucke, Julian | |
dc.contributor.author | Gray, Simon | |
dc.contributor.author | Castelluccio, Gustavo M. | |
dc.date.accessioned | 2024-02-14T09:46:41Z | |
dc.date.available | 2024-02-14T09:46:41Z | |
dc.date.issued | 2024-02-02 | |
dc.description.abstract | Stress corrosion cracking (SCC) can be detrimental to nickel-based superalloy components exposed to harsh environments in aero-gas turbines. During flight, engines consume contaminants deposited on the surface of a blade, often leading to degradation. Cracking can initiate within minutes and rapidly propagate, depending on the temperature, contaminants, and applied stress. This study investigated the interaction between cracks in single-crystal turbine blades at intermediate temperatures by integrating experimental and computational methods. We performed C-Ring tests to quantify the time required for cracking, along with microscopic characterisation of the damage. In parallel, we developed a finite-element simulation for C-Ring tests using a phase field model calibrated to match the location of the cracks. The results demonstrated that the crack's characteristic spacing and length determine the likelihood of shielding or coalescing mechanisms. | en_UK |
dc.description.sponsorship | The authors are grateful for the support from EPSRC Doctoral Training Partnership UK. | en_UK |
dc.identifier.citation | Elsherkisi M, Martinez FD, Mason-Flucke J, et al., (2024) Interaction of stress corrosion cracks in single crystals Ni-Base superalloys. Engineering Fracture Mechanics, Volume 298, March 2024, Article Number 109899 | en_UK |
dc.identifier.eissn | 1873-7315 | |
dc.identifier.issn | 0013-7944 | |
dc.identifier.uri | https://doi.org/10.1016/j.engfracmech.2024.109899 | |
dc.identifier.uri | https://dspace.lib.cranfield.ac.uk/handle/1826/20789 | |
dc.language.iso | en | en_UK |
dc.publisher | Elsevier | en_UK |
dc.rights | Attribution 4.0 International | * |
dc.rights.uri | http://creativecommons.org/licenses/by/4.0/ | * |
dc.subject | Phase field modelling | en_UK |
dc.subject | Nickel superalloys | en_UK |
dc.subject | Stress Corrosion Cracking | en_UK |
dc.subject | crack interactions | en_UK |
dc.subject | stress shielding | en_UK |
dc.title | Interaction of stress corrosion cracks in single crystals Ni-Base superalloys | en_UK |
dc.type | Article | en_UK |
dcterms.dateAccepted | 2024-01-25 |
Files
Original bundle
1 - 1 of 1
Loading...
- Name:
- Interaction_of_stress_corrosion_cracks-2024.pdf
- Size:
- 14.77 MB
- Format:
- Adobe Portable Document Format
- Description:
License bundle
1 - 1 of 1
No Thumbnail Available
- Name:
- license.txt
- Size:
- 1.63 KB
- Format:
- Item-specific license agreed upon to submission
- Description: