Fireside corrosion study of superheater materials in advanced power plants

dc.contributor.advisorSimms, Nigel J.
dc.contributor.advisorOakey, John
dc.contributor.authorSyed, Adnan
dc.date.accessioned2012-05-25T08:26:29Z
dc.date.available2012-05-25T08:26:29Z
dc.date.issued2011-10
dc.description.abstractConventional power plants are major emitters of CO2 gases, which are believed to be contributing to global warming. An efficient, co-firing biomass-coal power plant with oxy-firing combustion system (running at high steam temperature and pressure), can play a vital role in CO2 emission reduction. However, these techniques will further worsen the issue of fireside corrosion of heat exchangers. An increase in fireside corrosion rates can cause short component lives and unexpected failures if not dealt with appropriately. The aim of this PhD study was to use laboratory-based testing to assess the performance of alloy materials under superheater conditions in simulated co-fired (biomass and coal) air and oxy-fired combustion. In this PhD project five different alloys were used. Synthetic deposits were also prepared to simulate superheater deposit compositions. Tests were carried out at temperatures appropriate for metal temperatures in superheaters/reheaters of future power plants. The performance of samples was determined using: mass change data, advanced microscopy techniques, x-ray diffraction and dimensional metrology. Additional tests were carried out to investigate deposit stability and the effect of high concentrations of salts. The results achieved have confirmed the hypothesis that increased fireside corrosion rates are due to the combined effect of extreme environment: high temperatures, SO2 and HCl gases, aggressive deposits. Corrosion damage follows trends that resembles ‘bell-shaped’ curve in both air and oxy-fired conditions. Alloy corrosion damage in novel oxy-firing compared to air-firing conditions was significantly higher at 700C. The peak of the curve shifts from 650 to 700C in oxy-fired conditions. The alloys with higher chromium content clearly showed better corrosion resistance. The work on deposit chemistry and exposure to high salt concentrations has improved the understanding of corrosion reaction mechanisms. Corrosion damage data have been used to produce basic fireside corrosion mathematical model; which can be used as a stepping stone towards further development of fireside corrosion models.en_UK
dc.identifier.urihttp://dspace.lib.cranfield.ac.uk/handle/1826/7181
dc.language.isoenen_UK
dc.publisherCranfield Universityen_UK
dc.rights© Cranfield University 2011. All rights reserved. No part of this publication may be reproduced without the written permission of the copyright owner.en_UK
dc.titleFireside corrosion study of superheater materials in advanced power plantsen_UK
dc.typeThesis or dissertationen_UK
dc.type.qualificationlevelDoctoralen_UK
dc.type.qualificationnamePhDen_UK

Files

Original bundle
Now showing 1 - 1 of 1
Loading...
Thumbnail Image
Name:
Adnan_Syed_Thesis_2011.pdf
Size:
10.1 MB
Format:
Adobe Portable Document Format
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.79 KB
Format:
Item-specific license agreed upon to submission
Description: