Sub-surface damage issues for effective fabrication of large optics

A new ultra precision large optics grinding machine, BoX®has been developed at Cranfield University. BoX®islocated at the UK's Ultra Precision Surfaces laboratory at the OpTIC Technium. This machine offers a rapidand economic solution for grinding large off-axis aspherical and free-form optical components.This paper presents an analysis of subsurface damage assessments of optical ground materials produced usingdiamond resin bonded grinding wheels. The specific materials used, Zerodur®and ULE®are currently understudy for making extremely large telescope (ELT) segmented mirrors such as in the E-ELT project.The grinding experiments have been conducted on the BoX®grinding machine using wheels with grits sizes of76 μm, 46 μm and 25 μm. Grinding process data was collected using a Kistler dynamometer platform. Thehighest material removal rate (187.5 mm3/s) used ensures that a 1 metre diameter optic can be ground in lessthan 10 hours. The surface roughness and surface profile were measured using a Form Talysurf. The subsurfacedamage was revealed using a sub aperture polishing process in combination with an etching technique.These results are compared with the targeted form accuracy of 1 μm p-v over a 1 metre part, surface roughnessof 50-150 nm RMS and subsurface damage in the range of 2-5 μm. This process stage was validated on a 400mm ULE®blank and a 1 metre hexagonal Ze