Citation:
Gendre L., Njuguna J., Abhyankar H. and Ermini V. (2013). Mechanical properties of three-phase polyamide 6 nanocomposites. Proceedings of the 11th International Conference on Manufacturing Research (ICMR2013), Cranfield University, UK, 19th – 20th September 2013, pp 375-380
Abstract:
This work focus on the mechanical properties of three-phase nanocomposites using multiscale reinforcements. The influence of the nano-fillers content, as well as the temperature were studied. Polyamide-6 reinforced with short glass fibre 30 wt.% and with an addition of nanoclay (montmorillonite) and/or nanosilica (SiO2) were tested in order to characterise their tensile properties at room temperature and at 65oC just above the polyamide 6 glass transition temperature. SEM analysis were conducted on the fracture surface of the tensile bars. SEM investigations showed the importance of the interaction matrix/filler for the material behaviour. Our study also shows that the increase of OMMT percentage in polyamide-6/glass fibre composite made the material more brittle and had a negative effect on the tensile properties. Further, for the silica-based nanocomposites, an optimum was found for a nanofillers content of 1wt.%.