Citation:
Zhang Q, Zhao Y, Hao X, (2015), Phase structure tuned electrocaloric effect and pyroelectric energy harvesting performance of (Pb0.97La0.02)(Zr,Sn,Ti)O3 antiferroelectric thick films, Journal of Physical Chemistry C, Vol 119, iss 33, pp. 18877-18885
Abstract:
In present work, (100)-oriented (Pb0.97La0.02)(Zr0.95-xSnxTi0.05)O3 antiferroelectric thick films with x=0.08, 0.20 and 0.38, were successfully fabricated. These compositions are located in orthorhombic phase region, the morphotropic phase boundary (MPB), and tetragonal phase region, respectively. The effects of their phase structure on the electrocaloric effect and the pyroelectric energy harvesting behavior were investigated. A considerable temperature reduction of ∆T=13, 33, and 27 oC, due to the ferroelectric-antiferroelectric phase transition, was obtained at 25 oC in these thick films for x=0.08, 0.20, and 0.38, respectively. Moreover, a huge harvested energy density per cycle of W= 3.6, 6.8, and 4.0 J/cm3 was also realized under the experimental condition in the thick films with x=0.08, 0.20, and 0.38, respectively. These results indicated that both the cooling performance and the pyroelectric energy harvesting in antiferroelectrics could be optimized by the proper phase structure control.