Browsing by Author "Li, Yingjie"

Now showing 1 - 4 of 4
  • Thumbnail Image
    ItemOpen Access
    Attrition study of cement-supported biomass-activated calcium sorbents for CO2 capture
    (American Chemical Society, 2016-08-19) Duan, Lunbo; Yu, Zhijian; Erans Moreno, Maria; Li, Yingjie; Manovic, Vasilije; Anthony, Edward J.
    Enhanced CO2 capacity of biomass modified Ca-based sorbent has been reported recently, but undesired attrition resistance has also been observed. Cement was used as a support for biomass-activated calcium sorbent during the granulation process in this study, in order to improve the poor mechanical resistance. Attrition tests were carried out in an apparatus focused on impact breakage to evaluate how the biomass addition and cement support influence the particle strength during Ca-looping. Results showed biomass addition impaired the mechanical strength and cement support could improve it, which is reflected by the breakage probability and size change after impact of pellets experienced calcination and multiple calcination/carbonation cycles. Larger-sized particles suffered more intense attrition. The mechanical strength of sorbents declined significantly after higher temperature calcination but increased after carbonation. After multiple cycles, the mechanical strength of particles was greatly enhanced, but more cracks emerged. A semi-empirical formula for calculating average diameter after attrition based on Rittinger’s surface theory was developed. Observation on the morphology of particles indicated that particles with more porosity and cracks were more prone to breakage.
  • Thumbnail Image
    ItemOpen Access
    CO2 capture performance of calcium-based synthetic sorbent with hollow core-shell structure under calcium looping conditions
    (Elsevier, 2018-05-15) Ma, Xiaotong; Li, Yingjie; Duan, Lunbo; Anthony, Edward J.; Liu, Hantao
    A novel calcium-based synthetic CO2 sorbent with hollow core-shell structure was prepared by a carbon microsphere template route where carbide slag, alumina cement and glucose were employed as the low-cost calcium precursor, support and carbon source, respectively. The effects of the alumina cement addition, the pre-calcination temperature during the preparation process, the carbon template addition and calcination conditions on CO2 capture performances of the calcium-based synthetic sorbents were studied during calcium looping cycles. The synthetic sorbent containing 5 wt.% alumina cement possesses the highest CO2 capture capacity during calcium looping cycles, which is mainly composed of CaO and Ca12Al14O33. The CO2 capture capacities of the synthetic sorbent under mild and severe calcination conditions can retain 0.37 and 0.29 g/g after 20 cycles, which are 57% and 99% higher than those of carbide slag under the same conditions, respectively. The synthetic sorbent possesses a hollow micro-sphere morphology with a nano-structured shell and meso-porous structure, which decreases the diffusion resistance of CO2. Periodic density functional theory (DFT) calculations are used to explain why Ca12Al14O33 can effectively retard both agglomeration and sintering of the synthetic sorbent. The hollow core-shell model is proposed to explain the CO2 capture mechanism of the synthetic sorbent. For the same CO2 capture efficiency, the energy consumption in the calciner using the synthetic sorbent is much lower than those using carbide slag and natural limestone. This work designs a good method to prepare the hollow sphere-structured synthetic sorbents with high CO2 capture capacity and provides a promising way to integrate efficient CO2 capture with the utilization of industrial waste.
  • Thumbnail Image
    ItemOpen Access
    CO2 capture performance using biomass-templated cement-supported limestone pellets
    (American Chemical Society, 2016-09-09) Duan, Lunbo; Su, Chenglin; Erans Moreno, Maria; Li, Yingjie; Anthony, Edward J.; Chen, Huichao
    Synthetic biomass-templated cement-supported CaO-based sorbents were produced by granulation process for high-temperature post-combustion CO2 capture. Commercial flour was used as the biomass and served as a templating agent. The investigation of porosity showed that the pellets with biomass or cement resulted in enhancement of porosity. Four types of sorbents containing varying proportions of biomass and cement were subject to 20 cycles in a TGA under different calcination conditions. After first series of tests calcined at 850 °C in 100% N2, all composite sorbents clearly exhibited higher CO2 capture activity compared to untreated limestone with exception of sorbents doped by seawater. The biomass-templated cement-supported pellets exhibited the highest CO2 capture level of 46.5% relative to 20.8% for raw limestone after 20 cycles. However, the observed enhancement in performance was substantially reduced under 950 °C calcination condition. Considering the fact that both sorbents supported by cement exhibited relatively high conversion with a maximum value of 19.5%, cement promoted sorbents appear to be better at resisting of harsh calcination conditions. Although flour as biomass-templated material generated significantly enhancement in CO2 capture capacity, further exploration must be carried out to find the way of maintaining outstanding performance for CaO-based sorbents under severe reaction conditions.
  • Thumbnail Image
    ItemOpen Access
    Effect of steam hydration on reactivity and strength of cement-supported calcium sorbents for CO2 capture
    (Wiley, 2017-05-23) Yu, Zhijian; Duan, Lunbo; Su, Chenglin; Li, Yingjie; Anthony, Edward J.
    Steam hydration was used to reactivate spent cement-supported CO2 sorbent pellets for recycle and the effect of steam hydration on the reactivity of sorbents was investigated in a bubbling fluidised reactor. A specially designed impact apparatus was developed to evaluate the strength of the reactivated pellets as well as determine the effect of “superheating”. It was found that the reactivity of synthetic pellets was significantly elevated over that of raw limestone after steam hydration. The CaO conversion of spent pellets increased from 0.113 to 0.419 after hydration, whereas that of spent limestone ranged from 0.089 to 0.278. The CaO conversions of hydrated samples calcined under different conditions achieved the identical level, proportional to the degree of hydration. As expected, the mechanical strength of synthetic pellets declined severely after reactivation. Large cracks emerged on hydrated limestone as seen in scanning electron microscope images. By contrast, similar cracks were not observed for synthetic pellets after hydration, although hydration did produce higher porosity than seen with limestone and an increased surface area, which enhanced CO2 capacity and was associated with an increase in strength loss. The breakage rate of superheated steam-reactivated limestone derived pellets was about half that of hydrated samples. This demonstrates that superheating treatment (which allows the annealing of stacking faults and mechanical strain produced by hydration) enhances the strength of hydrated pellets. This work demonstrated that combining steam hydration with superheating can both reactivate the spent synthetic pellets and reduce strength decay associated with the hydration process.