Browsing by Author "Ermini, Valentina"

Now showing 1 - 2 of 2
  • Thumbnail Image
    ItemOpen Access
    The effect of nanoclay on dust generation during drilling process of polyamide 6 nanocomposites
    (Hindawi Publishing Corporation, 2012-06-10T00:00:00Z) Sachse, Sophia; Silva, Francesco; Zhu, Huijun; Irfan, Adeel; Leszczynska, Agneska; Pielichowski, Krzysztof; Ermini, Valentina; Blazquez, Maria; Kuzmenko, Oleksandr; Njuguna, James A. K.
    During the past decade, polymer nanocomposites have emerged as a novel and rapidly developing class of materials and attracted considerable investment in research and development worldwide. However, there is currently a lack of information available in the literature on the nano and ultrafine particle emission rates from these materials. In this study, influence of nanoclay on mechanical drilling of PA6 composites, in terms of dust generation has been reported. With the help of real-time characterization, submicrometer-sized particles (5.6-512 nm) size distribution and number concentration emitted from polyamide 6/nanoclay composites during mechanical drilling is studied. Total particle concentration for the PA6/nanoclay composites was 20,000 cm-3, while unreinforced panel measured a total concentration of approximately 400,000 cm-3. While the airborne particle concentration for the PA6/ nanoclay composites was 20 times lower than for the PA6 matrix, the concentration of deposited nanoparticles doubled for the nanocomposite. The results clearly shows that more particles in the size range between 175-350 nm are generated, during drilling of the nanocomposites and this particles deposit in a shorter time. It is likely that the presence of nanoclay in some way retains the formation of high quantity of airborne particles and promotes particle deposition.
  • Thumbnail Image
    ItemOpen Access
    Mechanical properties of three-phase polyamide 6 nanocomposites
    (Cranfield University Press, 2013-09-19) Gendre, Laura; Abhyankar, Hrushikesh; Njuguna, James; Ermini, Valentina
    This work focus on the mechanical properties of three-phase nanocomposites using multiscale reinforcements. The influence of the nano-fillers content, as well as the temperature were studied. Polyamide-6 reinforced with short glass fibre 30 wt.% and with an addition of nanoclay (montmorillonite) and/or nanosilica (SiO2) were tested in order to characterise their tensile properties at room temperature and at 65oC just above the polyamide 6 glass transition temperature. SEM analysis were conducted on the fracture surface of the tensile bars. SEM investigations showed the importance of the interaction matrix/filler for the material behaviour. Our study also shows that the increase of OMMT percentage in polyamide-6/glass fibre composite made the material more brittle and had a negative effect on the tensile properties. Further, for the silica-based nanocomposites, an optimum was found for a nanofillers content of 1wt.%.