Abstract:
Introduction
Previous work had shown that the conditions of grit blasting markedly
affected the reflectivity of a mild steel surface and that measurement of
reflectivity thus offered a method for the assessment of blasted surfaces.
The increase in reflectivity of a series of blasted specimens was found to
relate to decreasing surface quality and, after metal spraying, to
decreasing bond strength between the base and the sprayed metal. However,
one series of specimens did not show any correlation between reflectivity
and surface quality and it was decided that an examination of a considerable
number of specimens prepared under more carefully controlled conditions was
necessary for the next stage of the work.
The present report gives the results of reflectivity and bond strength
measurements on some 300 specimens of mild steel blasted under a number of
different conditions by three suppliers. Reflectivity measurements again
showed 'that specimens prepared by any one supplier could be placed in a
series of increasing reflectivity, although some difficulties were still
encountered in relating the result of different suppliers. These difficulties
were most marked with specimens blasted with worn grit. However, correlation
between reflectivity, pull-off strength and blasting conditions was good
with the series of specimens provided by two suppliers. The series from a
third supplier has not been fully tested yet, but very little difference in
reflectivity readings has been found.